Autor:

Mohammed Ali, Ghusoon Ridha ; Mubarak, Ethar Mohammed ; Al-Kalali, Rawaa Hamid ; Hussein, Emad Ali

Współtwórca:

Jurczak, Paweł - red.

Tytuł:

Friction stir lap welding of dissimilar aluminum alloys with copper particles ?additives

Tytuł publikacji grupowej:

IJAME, volume 29 (2024)

Temat i słowa kluczowe:

friction stir lap welding (FSLW) ; micro hardness ; copper ; AA1100 ; AA6061

Abstract:

Friction stir lap welding (FSLW) of dissimilar Aluminum alloys (AA1100 with AA6061) is ?investigated using a 3 ?mm sheet`s thick. These alloys are difference in physical characteristics, strength, and melting temperatures, at different tool ?rotation speeds (560, 900 and 1400) rpm and various feed rate (16, 40 and ??125) mm/min, with ?cylindrical pin geometry having two tilt angle: 0°, 3° was used. Copper particles were added ?to ?the weld zone to make composite friction stir welded joints using the best welding ?conditions. Many tests and ?inspections were carried out to evaluate the joint quality and the ?soundness of weldments. The highest value of tensile strength and efficiency at (1400, 40, 3°) while hardness recorded (97.5 HV) at stir zone of FSLW and it go downs along the HAZ and base metals of AA1100 and AA6061.

Wydawca:

Zielona Góra: Uniwersytet Zielonogórski

Data wydania:

2024

Typ zasobu:

artykuł

Format:

application/pdf

DOI:

10.59441/ijame/192531

Strony:

33-46

Źródło:

IJAME, volume 29, number 4 (2024)

Jezyk:

eng

Licencja:

CC 4.0

Licencja CC BY-NC-ND 4.0:

kliknij tutaj, żeby przejść

Prawa do dysponowania publikacją:

Biblioteka Uniwersytetu Zielonogórskiego