Search for: [Abstract = "It was found that the highest tensile strength \(223\) MPa at 1200 rpm rotational speed, 30 mm\/min traverse speed, 2.5 mm holes depth, and 1\/2 \(SiO2\/B4C\) nanoparticles mixing ratio, the highest hardness reached is \(155\) HV, then decreases in the direction of thermomechanically affected zone \(TMAZ\), heat affected zone \(HAZ\), and the base material at \(1200\) rpm rotational speed, \(30\) mm\/min linear speed, a hole depth of \(2\) mm and \(1\/3\) mixing ratio of \(B4C\/SiO2\) nanoparticles."]