Sivaraman, R. ; Jalil, Abduladheem Turki ; Aravindhan, Surendar ; Nan, Zhao ; Vini, M. Heydari ; Daneshmand, S.
In the present study, AA7075/Al2O3 composites have been fabricated via liquid metallurgy process. AA7075 alloy and Al2O3 particles were taken as the base matrix and reinforcements, respectively. Then, contents of 3 and 6 wt. % of Al2O3 subdivisions were added into the AA7075 matrix. ; To improve wettability and distribution, reinforcement particles were pre-heated to a temperature of 550°C for each composite sample. A hardened EN32 steel disc as the counter face was used to evaluate the wear rate pin-on-disc. The results showed that the wear rate of the AA/Al2O3 composites was smaller than that of the monolithic AA7075 samples. Finally, the worn surfaces of samples were investigated by SEM.
Zielona Góra: Uniwersytet Zielonogórski
IJAME, volume 27, number 4 (2022)
Biblioteka Uniwersytetu Zielonogórskiego
2023-07-06
2023-02-01
65
https://zbc.uz.zgora.pl/publication/77338
Nazwa wydania | Data |
---|---|
Fabrication of a high wear resistance AA7075/AL2O3 composites via liquid metallurgy process | 2023-07-06 |
Dylewicz, Weronika Szczotkarz, Natalia Maruda, Radosław Gupta, Munish Kumar Jurczak, Paweł - red.
Feldshtein, Eugene Dyachkova, Larisa Letsko, Andrey Kiełek, P. Kiełek, T. Jurczak, Paweł - red.
Hussein, Mohammed Ali Jurczak, Paweł - red.
Khandelwal, Ravi P. Chakrabarti, Anupam Bhargava, Pradeep Jurczak, Paweł - red.
Romanowicz, Marek Jurczak, Paweł - red.
Gąsiorek, Marek Jerzyniak, Stefan Świtka, Romuald - red.
Chetouh, Samir Ameur, T. Bouakba, M. Gaagaia, Djamel Edinne Khalfi, M. Safi, Brahim Jurczak, Paweł - red.
Pacha-Gołębiowska, Halina Piekarska, W. Jurczak, Paweł - red.